- 熔體流動速率 [g/10min]: 5.6
- 密度 [g/cm3]: 1.04
- 吸水率 [%]: 1.2
- 拉伸強度 [MPa]: 26.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | |
| Water Absorption | 1.2 % | 1.2 % | |
| Melt Flow | 5.6 g/10 min @Load 2.16 kg, Temperature 235 °C | 5.6 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 26.0 MPa | 3770 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 24 % | 24 % | 50 mm/min |
| Tensile Modulus | 0.465 GPa | 67.4 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 168 °C | 334 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||