- 熔體流動速率 [g/10min]: 61.3
- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 1.2
- 拉伸強度 [MPa]: 30.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 g/cc | 0.0372 lb/in3 | |
| Water Absorption | 1.2 % | 1.2 % | |
| Melt Flow | 61.3 g/10 min @Load 2.16 kg, Temperature 235 °C | 61.3 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 23 % | 23 % | 50 mm/min |
| Tensile Modulus | 0.560 GPa | 81.2 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 1.06 J/cm2 | 5.04 ft-lb/in2 | |
| 0.290 J/cm2 @Temperature -30.0 °C | 1.38 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Dissipation Factor | 0.000366 @Frequency 1e+6 Hz | 0.000366 @Frequency 1e+6 Hz | |
| 0.0013 @Frequency 100 Hz | 0.0013 @Frequency 100 Hz | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 168 °C | 334 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||