- 熔體流動速率 [g/10min]: 48.8
- 密度 [g/cm3]: 1.04
- 拉伸強度 [MPa]: 24.0
- 熱變形溫度 [℃]: 125.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in3 | |
| Melt Flow | 48.8 g/10 min @Load 2.16 kg, Temperature 235 °C | 48.8 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 24.0 MPa | 3480 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 26 % | 26 % | 50 mm/min |
| Tensile Modulus | 0.420 GPa | 60.9 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 2.50 J/cm2 | 11.9 ft-lb/in2 | |
| 0.360 J/cm2 @Temperature -30.0 °C | 1.71 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 ohm-cm | 1.00e+11 ohm-cm | |
| Surface Resistance | 5.00e+11 ohm | 5.00e+11 ohm | |
| Dielectric Strength | 24.0 kV/mm | 610 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 140 μm/m-°C @Temperature 20.0 °C | 77.8 μin/in-°F @Temperature 68.0 °F | |
| Melting Point | 168 °C | 334 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 125 °C | 257 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | |
| Vicat Softening Point | 132 °C | 270 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||