- 熔體流動速率 [g/10min]: 3.2
- 彎曲強度 [MPa]: 82.0
- 熱變形溫度 [℃]: 173.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 3.2 g/10 min @Load 2.16 kg, Temperature 235 °C | 3.2 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 82.0 MPa | 11900 psi | 5 mm/min |
| Elongation at Break | 6.0 % | 6.0 % | 5 mm/min |
| Tensile Modulus | 5.52 GPa | 801 ksi | 1 mm/min |
| Charpy Impact Unnotched | 6.81 J/cm2 | 32.4 ft-lb/in2 | |
| 6.28 J/cm2 @Temperature -30.0 °C | 29.9 ft-lb/in2 @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.37 J/cm2 | 6.52 ft-lb/in2 | |
| 0.810 J/cm2 @Temperature -30.0 °C | 3.85 ft-lb/in2 @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 60.0 μm/m-°C @Temperature 20.0 °C | 33.3 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 173 °C | 343 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 165 °C | 329 °F | |
| Vicat Softening Point | 165 °C | 329 °F | 50°C/hr; 50N |