- 熔體流動速率 [g/10min]: 2.2
- 密度 [g/cm3]: 1.17
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 1.07
- 拉伸強度 [MPa]: 69.0
- 斷裂伸長率 [%]: 134
- 彎曲強度 [MPa]: 60.0
- 彎曲模量 [MPa]: 4.00
- 硬度: 109.0
- 熱變形溫度 [℃]: 138.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.17 - 1.96 g/cc | 0.0423 - 0.0708 lb/in3 | Average value: 1.28 g/cc Grade Count:38 |
| Filler Content | 25.0 - 30.0 % | 25.0 - 30.0 % | Average value: 29.0 % Grade Count:5 |
| Water Absorption | 0.100 - 1.40 % | 0.100 - 1.40 % | Average value: 0.765 % Grade Count:21 |
| Moisture Absorption at Equilibrium | 0.500 - 0.600 % | 0.500 - 0.600 % | Average value: 0.569 % Grade Count:13 |
| Water Absorption at Saturation | 1.00 - 1.40 % | 1.00 - 1.40 % | Average value: 1.16 % Grade Count:8 |
| Linear Mold Shrinkage | 0.00100 - 0.00400 cm/cm | 0.00100 - 0.00400 in/in | Average value: 0.00231 cm/cm Grade Count:23 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00500 - 0.00550 cm/cm | 0.00500 - 0.00550 in/in | Average value: 0.00513 cm/cm Grade Count:4 |
| Linear Mold Shrinkage, Transverse | 0.00500 - 0.0110 cm/cm | 0.00500 - 0.0110 in/in | Average value: 0.00770 cm/cm Grade Count:10 |
| Melt Flow | 2.20 - 6.70 g/10 min | 2.20 - 6.70 g/10 min | Average value: 4.57 g/10 min Grade Count:6 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 109 - 110 | 109 - 110 | Average value: 110 Grade Count:4 |
| Hardness, Shore D | 77.0 - 83.0 | 77.0 - 83.0 | Average value: 80.6 Grade Count:6 |
| Ball Indentation Hardness | 120 - 155 MPa | 17400 - 22500 psi | Average value: 131 MPa Grade Count:7 |
| Tensile Strength, Ultimate | 60.0 - 130 MPa | 8700 - 18900 psi | Average value: 110 MPa Grade Count:27 |
| Tensile Strength, Yield | 69.0 - 130 MPa | 10000 - 18900 psi | Average value: 105 MPa Grade Count:11 |
| Elongation at Break | 3.00 - 12.0 % | 3.00 - 12.0 % | Average value: 5.52 % Grade Count:37 |
| Elongation at Yield | 3.00 - 4.00 % | 3.00 - 4.00 % | Average value: 3.67 % Grade Count:3 |
| Modulus of Elasticity | 4.00 - 8.82 GPa | 580 - 1280 ksi | Average value: 6.79 GPa Grade Count:33 |
| Flexural Yield Strength | 134 - 185 MPa | 19500 - 26800 psi | Average value: 156 MPa Grade Count:15 |
| Flexural Modulus | 4.00 - 7.10 GPa | 580 - 1030 ksi | Average value: 5.52 GPa Grade Count:18 |
| Compressive Yield Strength | 68.9 MPa | 10000 psi | Average value: 68.9 MPa Grade Count:3 |
| Izod Impact, Notched | 1.07 - 1.80 J/cm | 2.00 - 3.37 ft-lb/in | Average value: 1.34 J/cm Grade Count:14 |
| Izod Impact, Unnotched | 5.34 - 5340 J/cm | 10.0 - 10000 ft-lb/in | Average value: 7.32 J/cm Grade Count:9 |
| Izod Impact, Notched (ISO) | 10.0 - 17.0 kJ/m2 | 4.76 - 8.09 ft-lb/in2 | Average value: 14.5 kJ/m2 Grade Count:4 |
| Charpy Impact Unnotched | 5.00 - 10.0 J/cm2 | 23.8 - 47.6 ft-lb/in2 | Average value: 8.22 J/cm2 Grade Count:17 |
| 4.50 - 10.0 J/cm2 @Temperature -30.0 - 30.0 °C | 21.4 - 47.6 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 8.06 J/cm2 Grade Count:16 | |
| Charpy Impact, Notched | 1.00 - 2.50 J/cm2 | 4.76 - 11.9 ft-lb/in2 | Average value: 1.69 J/cm2 Grade Count:17 |
| 0.900 - 2.10 J/cm2 @Temperature -30.0 - 30.0 °C | 4.28 - 9.99 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 1.25 J/cm2 Grade Count:16 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1000 - 1.00e+15 ohm-cm | 1000 - 1.00e+15 ohm-cm | Average value: 1.99e+14 ohm-cm Grade Count:22 |
| Surface Resistance | 1000 - 1.00e+15 ohm | 1000 - 1.00e+15 ohm | Average value: 1.44e+14 ohm Grade Count:15 |
| Dielectric Constant | 3.40 - 4.10 | 3.40 - 4.10 | Average value: 3.86 Grade Count:6 |
| Dielectric Strength | 17.7 - 45.0 kV/mm | 450 - 1140 kV/in | Average value: 37.1 kV/mm Grade Count:16 |
| Dissipation Factor | 0.000345 - 0.0650 | 0.000345 - 0.0650 | Average value: 0.0227 Grade Count:9 |
| Comparative Tracking Index | 575 - 600 V | 575 - 600 V | Average value: 599 V Grade Count:16 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 80.0 μm/m-°C | 11.1 - 44.4 μin/in-°F | Average value: 43.3 μm/m-°C Grade Count:21 |
| CTE, linear, Transverse to Flow | 50.0 - 150 μm/m-°C | 27.8 - 83.3 μin/in-°F | Average value: 110 μm/m-°C Grade Count:9 |
| Thermal Conductivity | 0.160 - 0.432 W/m-K | 1.11 - 3.00 BTU-in/hr-ft2-°F | Average value: 0.342 W/m-K Grade Count:3 |
| Melting Point | 165 - 185 °C | 329 - 365 °F | Average value: 176 °C Grade Count:27 |
| Maximum Service Temperature, Air | 90.0 - 160 °C | 194 - 320 °F | Average value: 130 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 138 - 182 °C | 280 - 360 °F | Average value: 171 °C Grade Count:19 |
| Deflection Temperature at 1.8 MPa (264 psi) | 130 - 177 °C | 266 - 351 °F | Average value: 161 °C Grade Count:28 |
| Deflection Temperature at 8.0 MPa | 90.0 - 125 °C | 194 - 257 °F | Average value: 94.4 °C Grade Count:8 |
| Vicat Softening Point | 162 - 175 °C | 324 - 347 °F | Average value: 171 °C Grade Count:8 |
| Flammability, UL94 | HB - V-0 | HB - V-0 | Grade Count:32 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 - 266 °C | 420 - 510 °F | Average value: 241 °C Grade Count:5 |
| Mold Temperature | 65.6 - 104 °C | 150 - 220 °F | Average value: 85.0 °C Grade Count:7 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:7 |