- 熔體流動速率 [g/10min]: 3.2
- 密度 [g/cm3]: 1.11
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.908
- 斷裂伸長率 [%]: 96.0
- 彎曲強度 [MPa]: 38.0
- 彎曲模量 [MPa]: 3.45
- 熱變形溫度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 - 1.65 g/cc | 0.0401 - 0.0596 lb/in3 | Average value: 1.21 g/cc Grade Count:22 |
| Filler Content | 15.0 - 23.0 % | 15.0 - 23.0 % | Average value: 19.5 % Grade Count:4 |
| Water Absorption | 0.100 - 1.50 % | 0.100 - 1.50 % | Average value: 0.808 % Grade Count:13 |
| Moisture Absorption at Equilibrium | 0.500 - 0.800 % | 0.500 - 0.800 % | Average value: 0.575 % Grade Count:8 |
| Linear Mold Shrinkage | 0.00100 - 0.0120 cm/cm | 0.00100 - 0.0120 in/in | Average value: 0.00352 cm/cm Grade Count:16 |
| Linear Mold Shrinkage, Transverse | 0.00700 - 0.0120 cm/cm | 0.00700 - 0.0120 in/in | Average value: 0.00888 cm/cm Grade Count:8 |
| Melt Flow | 3.20 - 12.9 g/10 min | 3.20 - 12.9 g/10 min | Average value: 6.37 g/10 min Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 74.0 - 75.0 | 74.0 - 75.0 | Average value: 74.5 Grade Count:4 |
| Ball Indentation Hardness | 95.0 - 115 MPa | 13800 - 16700 psi | Average value: 107 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 38.0 - 110 MPa | 5510 - 16000 psi | Average value: 88.2 MPa Grade Count:25 |
| Elongation at Break | 3.00 - 37.0 % | 3.00 - 37.0 % | Average value: 7.74 % Grade Count:22 |
| Elongation at Yield | 2.70 - 5.00 % | 2.70 - 5.00 % | Average value: 3.60 % Grade Count:5 |
| Modulus of Elasticity | 2.00 - 9.40 GPa | 290 - 1360 ksi | Average value: 5.08 GPa Grade Count:23 |
| Flexural Yield Strength | 96.0 - 165 MPa | 13900 - 23900 psi | Average value: 128 MPa Grade Count:10 |
| Flexural Modulus | 3.45 - 8.00 GPa | 500 - 1160 ksi | Average value: 4.59 GPa Grade Count:12 |
| Izod Impact, Notched | 0.908 - 1.60 J/cm | 1.70 - 3.00 ft-lb/in | Average value: 1.23 J/cm Grade Count:8 |
| Izod Impact, Unnotched | 6.14 - 8.01 J/cm | 11.5 - 15.0 ft-lb/in | Average value: 7.14 J/cm Grade Count:4 |
| Charpy Impact Unnotched | 3.50 - 16.0 J/cm2 | 16.7 - 76.1 ft-lb/in2 | Average value: 7.12 J/cm2 Grade Count:17 |
| 3.50 - 16.0 J/cm2 @Temperature -30.0 - 30.0 °C | 16.7 - 76.1 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 7.53 J/cm2 Grade Count:12 | |
| Charpy Impact, Notched | 0.600 - 3.00 J/cm2 | 2.86 - 14.3 ft-lb/in2 | Average value: 1.44 J/cm2 Grade Count:13 |
| 0.600 - 2.00 J/cm2 @Temperature -30.0 - 30.0 °C | 2.86 - 9.52 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 0.996 J/cm2 Grade Count:13 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10000 - 1.00e+15 ohm-cm | 10000 - 1.00e+15 ohm-cm | Average value: 2.14e+14 ohm-cm Grade Count:10 |
| Surface Resistance | 1000 - 1.00e+12 ohm | 1000 - 1.00e+12 ohm | Average value: 4.65e+11 ohm Grade Count:11 |
| Insulation Resistance | 1.00e+9 - 1.00e+12 ohm | 1.00e+9 - 1.00e+12 ohm | Average value: 2.78e+11 ohm Grade Count:4 |
| Dielectric Strength | 17.5 - 44.0 kV/mm | 445 - 1120 kV/in | Average value: 31.6 kV/mm Grade Count:8 |
| Dissipation Factor | 0.000335 - 0.0380 | 0.000335 - 0.0380 | Average value: 0.0120 Grade Count:5 |
| Comparative Tracking Index | 100 - 600 V | 100 - 600 V | Average value: 520 V Grade Count:8 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 20.0 - 130 μm/m-°C | 11.1 - 72.2 μin/in-°F | Average value: 57.4 μm/m-°C Grade Count:11 |
| CTE, linear, Transverse to Flow | 80.0 - 150 μm/m-°C | 44.4 - 83.3 μin/in-°F | Average value: 133 μm/m-°C Grade Count:6 |
| Melting Point | 174 - 185 °C | 345 - 365 °F | Average value: 178 °C Grade Count:14 |
| Maximum Service Temperature, Air | 90.0 - 150 °C | 194 - 302 °F | Average value: 123 °C Grade Count:10 |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 - 180 °C | 302 - 356 °F | Average value: 169 °C Grade Count:7 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 - 165 °C | 131 - 329 °F | Average value: 145 °C Grade Count:11 |
| Deflection Temperature at 8.0 MPa | 80.0 - 110 °C | 176 - 230 °F | Average value: 86.0 °C Grade Count:5 |
| Vicat Softening Point | 151 - 175 °C | 304 - 347 °F | Average value: 165 °C Grade Count:5 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:13 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 - 266 °C | 420 - 510 °F | Average value: 244 °C Grade Count:8 |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | Average value: 255 °C Grade Count:4 |
| Melt Temperature | 190 - 274 °C | 374 - 525 °F | Average value: 237 °C Grade Count:6 |
| Mold Temperature | 40.0 - 110 °C | 104 - 230 °F | Average value: 83.3 °C Grade Count:9 |
| Drying Temperature | 75.0 - 110 °C | 167 - 230 °F | Average value: 90.8 °C Grade Count:6 |
| Injection Pressure | 40.0 - 103 MPa | 5800 - 15000 psi | Average value: 77.9 MPa Grade Count:5 |