- 熔體流動速率 [g/10min]: 3.0
- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 0.1
- 缺口沖擊強度: 0.481
- 斷裂伸長率 [%]: 90.0
- 彎曲強度 [MPa]: 60.0
- 彎曲模量 [MPa]: 3.00
- 熱變形溫度 [℃]: 163.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 - 1.29 g/cc | 0.0379 - 0.0466 lb/in3 | Average value: 1.14 g/cc Grade Count:26 |
| Filler Content | 10.0 - 50.0 % | 10.0 - 50.0 % | Average value: 25.5 % Grade Count:10 |
| Water Absorption | 0.100 - 1.10 % | 0.100 - 1.10 % | Average value: 0.378 % Grade Count:13 |
| Moisture Absorption at Equilibrium | 0.600 - 0.700 % | 0.600 - 0.700 % | Average value: 0.633 % Grade Count:3 |
| Linear Mold Shrinkage | 0.000200 - 0.00800 cm/cm | 0.000200 - 0.00800 in/in | Average value: 0.00246 cm/cm Grade Count:20 |
| Linear Mold Shrinkage, 6.35 mm section | 0.00200 - 0.00600 cm/cm | 0.00200 - 0.00600 in/in | Average value: 0.00367 cm/cm Grade Count:3 |
| Linear Mold Shrinkage, Transverse | 0.00100 - 0.00500 cm/cm | 0.00100 - 0.00500 in/in | Average value: 0.00300 cm/cm Grade Count:3 |
| Melt Flow | 3.00 - 6.00 g/10 min | 3.00 - 6.00 g/10 min | Average value: 3.95 g/10 min Grade Count:7 |
| Mechanical Properties | Metric | English | Comments |
| Ball Indentation Hardness | 100 - 135 MPa | 14500 - 19600 psi | Average value: 122 MPa Grade Count:3 |
| Tensile Strength, Ultimate | 60.0 - 250 MPa | 8700 - 36300 psi | Average value: 130 MPa Grade Count:24 |
| Elongation at Break | 1.50 - 5.00 % | 1.50 - 5.00 % | Average value: 3.18 % Grade Count:19 |
| Elongation at Yield | 2.50 - 9.00 % | 2.50 - 9.00 % | Average value: 4.98 % Grade Count:6 |
| Modulus of Elasticity | 3.50 - 23.0 GPa | 508 - 3340 ksi | Average value: 12.2 GPa Grade Count:24 |
| Flexural Yield Strength | 90.0 - 241 MPa | 13100 - 35000 psi | Average value: 175 MPa Grade Count:18 |
| Flexural Modulus | 3.00 - 20.0 GPa | 435 - 2900 ksi | Average value: 9.88 GPa Grade Count:18 |
| Izod Impact, Notched | 0.481 - 1.87 J/cm | 0.900 - 3.50 ft-lb/in | Average value: 1.02 J/cm Grade Count:12 |
| Izod Impact, Unnotched | 4.81 - 10.7 J/cm | 9.00 - 20.0 ft-lb/in | Average value: 6.92 J/cm Grade Count:11 |
| Charpy Impact Unnotched | 3.50 - 7.00 J/cm2 | 16.7 - 33.3 ft-lb/in2 | Average value: 5.62 J/cm2 Grade Count:13 |
| 4.00 - 6.00 J/cm2 @Temperature -30.0 - 30.0 °C | 19.0 - 28.6 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 5.50 J/cm2 Grade Count:7 | |
| Charpy Impact, Notched | 1.00 - 2.80 J/cm2 | 4.76 - 13.3 ft-lb/in2 | Average value: 1.58 J/cm2 Grade Count:11 |
| 0.500 - 1.80 J/cm2 @Temperature -30.0 - 30.0 °C | 2.38 - 8.57 ft-lb/in2 @Temperature -22.0 - 86.0 °F | Average value: 0.993 J/cm2 Grade Count:7 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 10.0 - 1.00e+6 ohm-cm | 10.0 - 1.00e+6 ohm-cm | Average value: 63100 ohm-cm Grade Count:10 |
| Surface Resistance | 50.0 - 1.00e+11 ohm | 50.0 - 1.00e+11 ohm | Average value: 1.00e+10 ohm Grade Count:10 |
| Insulation Resistance | 100 - 1.00e+11 ohm | 100 - 1.00e+11 ohm | Average value: 1.67e+10 ohm Grade Count:6 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 10.0 - 48.6 μm/m-°C | 5.56 - 27.0 μin/in-°F | Average value: 29.1 μm/m-°C Grade Count:7 |
| CTE, linear, Transverse to Flow | 50.0 - 150 μm/m-°C | 27.8 - 83.3 μin/in-°F | Average value: 110 μm/m-°C Grade Count:3 |
| Melting Point | 174 - 179 °C | 345 - 354 °F | Average value: 176 °C Grade Count:8 |
| Maximum Service Temperature, Air | 90.0 - 150 °C | 194 - 302 °F | Average value: 118 °C Grade Count:8 |
| Deflection Temperature at 0.46 MPa (66 psi) | 163 - 175 °C | 325 - 347 °F | Average value: 171 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 154 - 177 °C | 310 - 350 °F | Average value: 166 °C Grade Count:11 |
| Deflection Temperature at 8.0 MPa | 100 - 160 °C | 212 - 320 °F | Average value: 128 °C Grade Count:3 |
| Vicat Softening Point | 170 °C | 338 °F | Average value: 170 °C Grade Count:4 |
| Flammability, UL94 | HB | HB | Grade Count:17 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 - 266 °C | 420 - 510 °F | Average value: 246 °C Grade Count:11 |
| Nozzle Temperature | 250 - 260 °C | 482 - 500 °F | Average value: 255 °C Grade Count:6 |
| Melt Temperature | 221 - 274 °C | 430 - 525 °F | Average value: 249 °C Grade Count:12 |
| Mold Temperature | 65.6 - 110 °C | 150 - 230 °F | Average value: 86.8 °C Grade Count:17 |
| Drying Temperature | 75.0 - 105 °C | 167 - 221 °F | Average value: 86.5 °C Grade Count:12 |
| Dry Time | 4.00 hour | 4.00 hour | Average value: 4.00 hour Grade Count:4 |
| Moisture Content | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:6 |
| Dew Point | -40.0 °C | -40.0 °F | Average value: -40.0 °C Grade Count:6 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:11 |