- 密度 [g/cm3]: 1.03
- 吸水率 [%]: 0.1
- 缺口沖擊強(qiáng)度: 0.374
- 斷裂伸長率 [%]: 37.9
- 彎曲強(qiáng)度 [MPa]: 31.0
- 彎曲模量 [MPa]: 1.10
- 硬度: 106.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.03 - 1.14 g/cc | 0.0372 - 0.0412 lb/in3 | Average value: 1.10 g/cc Grade Count:10 |
| Water Absorption | 0.100 - 0.500 % | 0.100 - 0.500 % | Average value: 0.229 % Grade Count:7 |
| Linear Mold Shrinkage | 0.00700 - 0.0200 cm/cm | 0.00700 - 0.0200 in/in | Average value: 0.0133 cm/cm Grade Count:10 |
| Linear Mold Shrinkage, 6.35 mm section | 0.0160 - 0.0180 cm/cm | 0.0160 - 0.0180 in/in | Average value: 0.0170 cm/cm Grade Count:3 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 106 - 108 | 106 - 108 | Average value: 107 Grade Count:3 |
| Tensile Strength, Ultimate | 31.0 - 50.0 MPa | 4500 - 7250 psi | Average value: 40.8 MPa Grade Count:9 |
| Elongation at Break | 4.50 - 20.0 % | 4.50 - 20.0 % | Average value: 10.6 % Grade Count:8 |
| Modulus of Elasticity | 1.24 - 2.30 GPa | 180 - 334 ksi | Average value: 1.65 GPa Grade Count:8 |
| Flexural Yield Strength | 37.9 - 75.0 MPa | 5500 - 10900 psi | Average value: 56.4 MPa Grade Count:10 |
| Flexural Modulus | 1.10 - 2.00 GPa | 160 - 290 ksi | Average value: 1.48 GPa Grade Count:10 |
| Izod Impact, Notched | 0.374 - 0.801 J/cm | 0.700 - 1.50 ft-lb/in | Average value: 0.618 J/cm Grade Count:8 |
| Izod Impact, Unnotched | 8.01 - 5340 J/cm | 15.0 - 10000 ft-lb/in | Average value: 11.3 J/cm Grade Count:6 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+11 - 1.00e+13 ohm-cm | 1.00e+11 - 1.00e+13 ohm-cm | Average value: 3.70e+12 ohm-cm Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 1.8 MPa (264 psi) | 49.0 - 77.8 °C | 120 - 172 °F | Average value: 60.6 °C Grade Count:7 |
| Flammability, UL94 | HB | HB | Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 216 - 266 °C | 420 - 510 °F | Average value: 244 °C Grade Count:5 |
| Melt Temperature | 221 - 274 °C | 430 - 525 °F | Average value: 249 °C Grade Count:5 |
| Mold Temperature | 65.6 - 110 °C | 150 - 230 °F | Average value: 86.3 °C Grade Count:8 |
| Drying Temperature | 75.0 - 105 °C | 167 - 221 °F | Average value: 85.5 °C Grade Count:5 |
| Dry Time | 4.00 hour | 4.00 hour | Average value: 4.00 hour Grade Count:3 |
| Moisture Content | 0.100 % | 0.100 % | Average value: 0.100 % Grade Count:3 |
| Dew Point | -40.0 °C | -40.0 °F | Average value: -40.0 °C Grade Count:3 |
| Injection Pressure | 68.9 - 103 MPa | 10000 - 15000 psi | Average value: 86.2 MPa Grade Count:6 |