- 熔體流動速率 [g/10min]: 2.1
- 密度 [g/cm3]: 1.02
- 拉伸強(qiáng)度 [MPa]: 39.0
- 熱變形溫度 [℃]: 143.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.02 - 1.08 g/cc | 0.0368 - 0.0390 lb/in3 | Average value: 1.05 g/cc Grade Count:5 |
| Melt Flow | 2.10 - 61.5 g/10 min | 2.10 - 61.5 g/10 min | Average value: 31.8 g/10 min Grade Count:4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 39.0 - 50.0 MPa | 5660 - 7250 psi | Average value: 44.8 MPa Grade Count:4 |
| Elongation at Break | 5.00 - 50.0 % | 5.00 - 50.0 % | Average value: 37.6 % Grade Count:5 |
| Elongation at Yield | 5.00 - 12.0 % | 5.00 - 12.0 % | Average value: 8.50 % Grade Count:4 |
| Modulus of Elasticity | 1.36 - 8.00 GPa | 197 - 1160 ksi | Average value: 3.09 GPa Grade Count:5 |
| Charpy Impact Unnotched | 6.00 J/cm2 - NB | 28.6 ft-lb/in2 - NB | Average value: 9.65 J/cm2 Grade Count:4 |
| 7.00 - 11.1 J/cm2 @Temperature -30.0 - -30.0 °C | 33.3 - 52.8 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 9.05 J/cm2 Grade Count:2 | |
| Charpy Impact, Notched | 0.410 - 1.40 J/cm2 | 1.95 - 6.66 ft-lb/in2 | Average value: 0.675 J/cm2 Grade Count:4 |
| 0.400 - 1.30 J/cm2 @Temperature -30.0 - -30.0 °C | 1.90 - 6.19 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.635 J/cm2 Grade Count:4 | |
| Electrical Properties | Metric | English | Comments |
| Comparative Tracking Index | 100 - 600 V | 100 - 600 V | Average value: 433 V Grade Count:3 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 80.0 - 150 μm/m-°C | 44.4 - 83.3 μin/in-°F | Average value: 103 μm/m-°C Grade Count:3 |
| Melting Point | 174 - 178 °C | 345 - 352 °F | Average value: 175 °C Grade Count:5 |
| Deflection Temperature at 0.46 MPa (66 psi) | 143 - 175 °C | 289 - 347 °F | Average value: 160 °C Grade Count:3 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 - 170 °C | 149 - 338 °F | Average value: 100 °C Grade Count:3 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:5 |