- 熔體流動速率 [g/10min]: 1.9
- 密度 [g/cm3]: 1.0
- 吸水率 [%]: 1.0
- 拉伸強度 [MPa]: 20.0
- 熱變形溫度 [℃]: 90.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.00 - 1.04 g/cc | 0.0361 - 0.0376 lb/in3 | Average value: 1.02 g/cc Grade Count:26 |
| Water Absorption | 1.00 - 2.30 % | 1.00 - 2.30 % | Average value: 1.41 % Grade Count:9 |
| Moisture Absorption at Equilibrium | 0.500 - 0.700 % | 0.500 - 0.700 % | Average value: 0.550 % Grade Count:14 |
| Water Absorption at Saturation | 1.00 - 1.50 % | 1.00 - 1.50 % | Average value: 1.20 % Grade Count:6 |
| Melt Flow | 1.90 - 170 g/10 min | 1.90 - 170 g/10 min | Average value: 26.4 g/10 min Grade Count:23 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 20.0 - 76.0 MPa | 2900 - 11000 psi | Average value: 39.5 MPa Grade Count:34 |
| Elongation at Break | 50.0 - 400 % | 50.0 - 400 % | Average value: 86.7 % Grade Count:39 |
| Elongation at Yield | 5.00 - 32.0 % | 5.00 - 32.0 % | Average value: 16.1 % Grade Count:30 |
| Modulus of Elasticity | 0.350 - 2.23 GPa | 50.8 - 323 ksi | Average value: 1.05 GPa Grade Count:34 |
| Charpy Impact Unnotched | 1000 J/cm2 - NB | 4760 ft-lb/in2 - NB | Grade Count:27 |
| NB - NB @Temperature -30.0 - -30.0 °C | NB - NB @Temperature -22.0 - -22.0 °F | Grade Count:12 | |
| Charpy Impact, Notched | 0.400 J/cm2 - NB | 1.90 ft-lb/in2 - NB | Average value: 1.85 J/cm2 Grade Count:25 |
| 0.250 - 1.24 J/cm2 @Temperature -30.0 - -30.0 °C | 1.19 - 5.90 ft-lb/in2 @Temperature -22.0 - -22.0 °F | Average value: 0.640 J/cm2 Grade Count:24 | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 2.00e+8 - 1.00e+15 ohm-cm | 2.00e+8 - 1.00e+15 ohm-cm | Average value: 9.97e+13 ohm-cm Grade Count:20 |
| Surface Resistance | 1.00e+11 - 1.00e+15 ohm | 1.00e+11 - 1.00e+15 ohm | Average value: 3.55e+14 ohm Grade Count:20 |
| Dielectric Constant | 3.00 - 15.0 | 3.00 - 15.0 | Average value: 5.83 Grade Count:12 |
| Dielectric Strength | 24.0 - 50.0 kV/mm | 610 - 1270 kV/in | Average value: 34.7 kV/mm Grade Count:21 |
| Dissipation Factor | 0.000304 - 0.330 | 0.000304 - 0.330 | Average value: 0.0916 Grade Count:14 |
| Comparative Tracking Index | 575 - 600 V | 575 - 600 V | Average value: 597 V Grade Count:17 |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 50.0 - 150 μm/m-°C | 27.8 - 83.3 μin/in-°F | Average value: 96.4 μm/m-°C Grade Count:20 |
| CTE, linear, Transverse to Flow | 100 μm/m-°C | 55.6 μin/in-°F | Average value: 100 μm/m-°C Grade Count:6 |
| Melting Point | 168 - 178 °C | 334 - 352 °F | Average value: 174 °C Grade Count:14 |
| Maximum Service Temperature, Air | 75.0 - 150 °C | 167 - 302 °F | Average value: 113 °C Grade Count:3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 90.0 - 135 °C | 194 - 275 °F | Average value: 113 °C Grade Count:14 |
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 - 165 °C | 104 - 329 °F | Average value: 56.3 °C Grade Count:20 |
| Vicat Softening Point | 115 - 142 °C | 239 - 288 °F | Average value: 131 °C Grade Count:15 |
| Flammability, UL94 | HB - V-2 | HB - V-2 | Grade Count:21 |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80.0 % | 80.0 % | Average value: 80.0 % Grade Count:4 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 230 °C | 446 °F | Average value: 230 °C Grade Count:5 |
| Feed Temperature | 40.0 °C | 104 °F | Average value: 40.0 °C Grade Count:5 |
| Die Temperature | 230 °C | 446 °F | Average value: 230 °C Grade Count:5 |
| Melt Temperature | 190 - 240 °C | 374 - 464 °F | Average value: 220 °C Grade Count:5 |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | Average value: 50.0 °C Grade Count:5 |
| Injection Velocity | 100 mm/sec | 3.94 in/sec | Average value: 100 mm/sec Grade Count:5 |
| Die Opening | 0.0400 cm | 0.0157 in | Average value: 0.0400 cm Grade Count:5 |
| Roll Temperature | 50.0 °C | 122 °F | Average value: 50.0 °C Grade Count:5 |
| Drying Temperature | 80.0 - 110 °C | 176 - 230 °F | Average value: 96.7 °C Grade Count:5 |
| Dry Time | 2.00 - 8.00 hour | 2.00 - 8.00 hour | Average value: 5.00 hour Grade Count:5 |
| Injection Pressure | 40.0 - 50.0 MPa | 5800 - 7250 psi | Average value: 45.0 MPa Grade Count:5 |
| Hold Pressure | 25.0 - 50.0 MPa | 3630 - 7250 psi | Average value: 37.5 MPa Grade Count:5 |
| Back Pressure | 5.00 MPa | 725 psi | Average value: 5.00 MPa Grade Count:5 |
| Screw Speed | 15.0 - 76.0 rpm | 15.0 - 76.0 rpm | Average value: 45.5 rpm Grade Count:5 |