- 密度 [g/cm3]: 1.06
- 吸水率 [%]: 3.2
- 拉伸強(qiáng)度 [MPa]: 78.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | |
| Water Absorption | 3.2 % | 3.2 % | |
| High Load Melt Index | 4.9 g/10 min @Load 21.6 kg, Temperature 235 °C | 4.9 g/10 min @Load 47.6 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 78.0 MPa | 11300 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min |
| Tensile Modulus | 2.11 GPa | 306 ksi | 1 mm/min |
| Thermal Properties | Metric | English | Comments |
| Glass Transition Temp, Tg | 170 °C | 338 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | ||
| Oxygen Index | 26 % | 26 % | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |