- 密度 [g/cm3]: 1.06
- 拉伸強度 [MPa]: 75.0
- 熱變形溫度 [℃]: 150.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.06 g/cc | 0.0383 lb/in3 | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min |
| Tensile Modulus | 2.09 GPa | 303 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 1.48 J/cm2 | 7.04 ft-lb/in2 | |
| 1.33 J/cm2 @Temperature -30.0 °C | 6.33 ft-lb/in2 @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | |
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | |
| Dielectric Constant | 3.0 @Frequency 100 Hz | 3.0 @Frequency 100 Hz | |
| Dielectric Strength | 50.0 kV/mm | 1270 kV/in | |
| Dissipation Factor | 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 70.0 μm/m-°C @Temperature 20.0 °C | 38.9 μin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 135 °C | 275 °F | |
| Vicat Softening Point | 160 °C | 320 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |
| V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | ||
| Oxygen Index | 26 % | 26 % | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |