Cresset Powers Cress-Alon? NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH

Cresset Powers Cress-Alon? NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH 物性表: Cresset Powers Cress-Alon? NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH物性表及特性介紹,Cresset Powers Cress-Alon? NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH注塑參數詳情,如需Cresset Powers Cress-Alon? NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH下載, 可到相關下載區下載

熔體流動速率 [g/10min]: 48.3
密度 [g/cm3]: 1.15
缺口沖擊強度: 0.38
拉伸強度 [MPa]: 96.0
斷裂伸長率 [%]: 143
彎曲強度 [MPa]: 96.0
彎曲模量 [MPa]: 3.70

Physical Properties	Metric	English	Comments

Density	1.15 g/cc	0.0415 lb/in3	ASTM D792
Viscosity Measurement	2.7	2.7	Relative Viscosity
Melt Flow	48.3 g/10 min @Load 5.00 kg, Temperature 235 °C	48.3 g/10 min @Load 11.0 lb, Temperature 455 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	96.0 MPa	13900 psi	ASTM D638
Tensile Strength, Yield	96.0 MPa	13900 psi	ASTM D638
Elongation at Break	2.3 %	2.3 %	ASTM D638
Elongation at Yield	2.4 %	2.4 %	ASTM D638
Flexural Yield Strength	143 MPa	20700 psi	ASTM D790
Flexural Modulus	3.70 GPa	537 ksi	ASTM D790
Izod Impact, Notched	0.380 J/cm	0.712 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	221 °C	430 °F	ASTM DSC

關鍵詞:
供應
PA6
50% RH
Cresset Powers Cress-Alon? NE2740 4% Nano Clay Loaded
2.7 r.v. Compounding Grade Nylon 6

轉載請注明: 轉自中國塑膠原料之家 http://www.spnmy.cn/wuxingbiao/

本文鏈接: http://www.spnmy.cn/yuanliaoku/show-46480.html

免責聲明: 本文 Cresset Powers Cress-Alon? NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH 僅代表作者個人觀點，中國塑膠原料之家無關。中國塑膠原料之家網所轉載的內容，其版權均由原作者和資料提供方所擁有！如因作品版權問題需要處理，請與我們聯絡

該類別其他物性信息