- 熔體流動(dòng)速率 [g/10min]: 14.0
- 密度 [g/cm3]: 1.13
- 缺口沖擊強(qiáng)度: 0.28
- 拉伸強(qiáng)度 [MPa]: 90.0
- 斷裂伸長(zhǎng)率 [%]: 117
- 彎曲模量 [MPa]: 3.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ASTM D792 |
| Viscosity Measurement | 3.0 | 3.0 | Relative Viscosity |
| Melt Flow | 14 g/10 min @Load 5.00 kg, Temperature 230 °C | 14 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 80 % | 80 % | ASTM D638 |
| Elongation at Yield | 3.9 % | 3.9 % | ASTM D638 |
| Flexural Yield Strength | 117 MPa | 17000 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.280 J/cm | 0.525 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 221 °C | 430 °F | ASTM DSC |