- 熔體流動速率 [g/10min]: 10.0
- 密度 [g/cm3]: 1.19
- 缺口沖擊強度: 0.1
- 彎曲模量 [MPa]: 3.80
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.19 g/cc | 0.0430 lb/in3 | ISO 1183 |
| Linear Mold Shrinkage | 0.0030 - 0.0060 cm/cm | 0.0030 - 0.0060 in/in | ISO 2577 |
| Melt Flow | 10 g/10 min @Load 10.0 kg, Temperature 240 °C | 10 g/10 min @Load 22.0 lb, Temperature 464 °F | ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 65.0 MPa | 9430 psi | ISO 527 |
| Elongation at Break | 2.6 % | 2.6 % | ISO 527 |
| Tensile Modulus | 5.20 GPa | 754 ksi | ISO 527 |
| Flexural Modulus | 3.80 GPa | 551 ksi | ISO 178 |
| Izod Impact, Notched | 0.100 J/cm @Temperature 23.0 °C | 0.187 ft-lb/in @Temperature 73.4 °F | ISO 180/A |
| Thermal Properties | Metric | English | Comments |
| Vicat Softening Point | 112 °C @Load 5.00 kg | 234 °F @Load 11.0 lb | 50°C/hr; ISO 306 |
| 189 °C @Load 0.999 kg | 372 °F @Load 2.20 lb | 50°C/hr; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||