- 熔體流動速率 [g/10min]: 8.9
- 密度 [g/cm3]: 1.15
- 缺口沖擊強度: 0.27
- 拉伸強度 [MPa]: 90.0
- 斷裂伸長率 [%]: 155
- 彎曲模量 [MPa]: 4.20
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.15 g/cc | 0.0415 lb/in3 | ASTM D792 |
| Viscosity Measurement | 3.0 | 3.0 | Relative Viscosity |
| Melt Flow | 8.9 g/10 min @Load 5.00 kg, Temperature 230 °C | 8.9 g/10 min @Load 11.0 lb, Temperature 446 °F | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | ASTM D638 |
| Elongation at Break | 3.2 % | 3.2 % | ASTM D638 |
| Elongation at Yield | 2.0 % | 2.0 % | ASTM D638 |
| Flexural Yield Strength | 155 MPa | 22500 psi | ASTM D790 |
| Flexural Modulus | 4.20 GPa | 609 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256, Notch |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 221 °C | 430 °F | ASTM DSC |