- 熔體流動速率 [g/10min]: 121.0
- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 8.5
- 拉伸強度 [MPa]: 35.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in3 | ISO 1183 | ||
| Water Absorption | 8.5 - 9.5 % | 8.5 - 9.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.1 - 2.9 % | 2.1 - 2.9 % | (23°C/50% R.H.); ISO 62 | ||
| Melt Flow | 121 g/10 min @Load 5.00 kg, Temperature 275 °C | 121 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 35.0 MPa | 5080 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 18 % | 18 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 0.900 GPa | 131 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | NB | NB | ISO 180/A | ||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| Charpy Impact, Notched | NB | NB | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 550 MPa | 79800 psi | ISO 899 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 6.4 @Frequency 1.00e+6 Hz | 6.4 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.24 @Frequency 1.00e+6 Hz | 0.24 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.320 W/m-K | 2.22 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 160 °C | 320 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Release agent | |||||