- 熔體流動(dòng)速率 [g/10min]: 181.0
- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 9.0
- 缺口沖擊強(qiáng)度: 5.5
- 拉伸強(qiáng)度 [MPa]: 85.0
- 彎曲模量 [MPa]: 2.60
- 熱變形溫度 [℃]: 180.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 | ||
| Water Absorption | 9.0 - 10 % | 9.0 - 10 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.6 - 3.4 % | 2.6 - 3.4 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 150 cm3/g | 150 cm3/g | Viscosity number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | |||
| Melt Flow | 181 g/10 min @Load 5.00 kg, Temperature 275 °C | 181 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 85.0 MPa | 12300 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 3.00 GPa | 435 ksi | ISO 527 | ||
| Flexural Modulus | 2.60 GPa | 377 ksi | ISO 178 | ||
| 2.80 GPa | 406 ksi | ISO 178 | |||
| Izod Impact, Notched (ISO) | 5.50 kJ/m2 | 2.62 ft-lb/in2 | ISO 180/A | ||
| 5.00 kJ/m2 @Temperature -30.0 °C | 2.38 ft-lb/in2 @Temperature -22.0 °F | ISO 180/A | |||
| Charpy Impact Unnotched | NB | NB | ISO 179/1eU | ||
| 10.0 J/cm2 @Temperature -30.0 °C | 47.6 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.550 J/cm2 | 2.62 ft-lb/in2 | ISO 179/1eA | ||
| 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.023 @Frequency 1.00e+6 Hz | 0.023 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.700 - 1.00 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.389 - 0.556 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | |||
| Thermal Conductivity | 0.330 W/m-K | 2.29 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 100 °C | 212 °F | for 50% loss of tensile strength after 20,000 hr | ||
| 112 °C | 234 °F | for 50% loss of tensile strength after 5,000 hr | |||
| 180 °C | 356 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 250 - 270 °C | 482 - 518 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| Release agent | |||||
| U.V. stabilized or stable to weather | |||||