- 熔體流動速率 [g/10min]: 145.0
- 密度 [g/cm3]: 1.13
- 缺口沖擊強度: 0.53
- 拉伸強度 [MPa]: 79.0
- 彎曲模量 [MPa]: 2.74
- 熱變形溫度 [℃]: 180.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 | ||
| Relative Viscosity | 2.7 cP | 2.7 cP | ISO Test; 96 % SAV | ||
| Viscosity Test | 150 cm3/g | 150 cm3/g | Viscosity number | ||
| Melt Flow | 145 g/10 min @Load 5.00 kg, Temperature 275 °C | 145 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 79.0 MPa | 11500 psi | 50mm/min; ISO 527 | ||
| 79.0 MPa | 11500 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | 4.2 % | 4.2 % | 2 in/min; ASTM Test | ||
| Elongation at Yield | 4.2 % | 4.2 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 1.107 GPa | 160.6 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 2.74 GPa | 397 ksi | ASTM Test | ||
| Izod Impact, Notched | 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 215 °C | 419 °F | ASTM Test | ||
| 220 °C | 428 °F | 10 K/min | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 180 °C | 356 °F | ASTM Test | ||
| 180 °C | 356 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 76.0 °C | 169 °F | ASTM Test | ||
| 76.0 °C | 169 °F | ISO 75 | |||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||