- 熔體流動速率 [g/10min]: 78.65
- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 5.4
- 缺口沖擊強度: 16.0
- 拉伸強度 [MPa]: 205.0
- 彎曲模量 [MPa]: 10.5
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ISO 1183 | ||
| Water Absorption | 5.4 - 6.0 % | 5.4 - 6.0 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.6 - 2.0 % | 1.6 - 2.0 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 140 cm3/g | 140 cm3/g | Viscosity number; ISO 307 | ||
| Melt Flow | 78.65 g/10 min @Load 5.00 kg, Temperature 275 °C | 78.65 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 205 MPa | 29700 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 2.8 % | 2.8 % | 50mm/min; ISO 527 | ||
| Flexural Strength | 290 MPa | 42100 psi | ISO 178 | ||
| Flexural Modulus | 10.5 GPa | 1520 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 16.0 kJ/m2 | 7.61 ft-lb/in2 | ISO 180/A | ||
| 12.0 kJ/m2 @Temperature -30.0 °C | 5.71 ft-lb/in2 @Temperature -22.0 °F | ISO 180/A | |||
| Charpy Impact Unnotched | 9.00 J/cm2 | 42.8 ft-lb/in2 | ISO 179/1eU | ||
| 8.50 J/cm2 @Temperature -30.0 °C | 40.5 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.40 J/cm2 | 6.66 ft-lb/in2 | ISO 179/1eA | ||
| 1.10 J/cm2 @Temperature -30.0 °C | 5.24 ft-lb/in2 @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 4.0 @Frequency 1.00e+6 Hz | 4.0 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.014 @Frequency 100 Hz | 0.014 @Frequency 100 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.100 - 0.150 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.0556 - 0.0833 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.550 - 0.700 μm/m-°C @Temperature 23.0 - 80.0 °C | 0.306 - 0.389 μin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.40 J/g-°C | 0.335 BTU/lb-°F | |||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft2-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 200 °C | 392 °F | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | BK00564 | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||