- 熔體流動速率 [g/10min]: 130.0
- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 9.5
- 缺口沖擊強度: 0.48
- 拉伸強度 [MPa]: 80.0
- 熱變形溫度 [℃]: 160.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | ISO 1183 | ||
| Water Absorption | 9.5 % | 9.5 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 23°C/50% R.H.; ISO 62 | ||
| Relative Viscosity | 2.7 cP | 2.7 cP | ISO Test; 96 % SAV | ||
| Viscosity Test | 150 cm3/g | 150 cm3/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM Data; MD | ||
| Melt Flow | 130 g/10 min @Load 5.00 kg, Temperature 275 °C | 130 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | 2 in/min; ASTM Test | ||
| 90.0 MPa | 13100 psi | 50mm/min; ISO 527 | |||
| Elongation at Break | 15 % | 15 % | 50mm/min, Nominal strain; ISO 527 | ||
| Elongation at Yield | 4.5 % | 4.5 % | 50mm/min; ISO 527 | ||
| Tensile Modulus | 3.00 GPa | 435 ksi | 1mm/min; ISO 527 | ||
| 3.00 GPa | 435 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.480 J/cm @Temperature -40.0 °C | 0.899 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 0.530 J/cm @Thickness 3.17 mm | 0.993 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Charpy Impact Unnotched | NB | NB | ISO 179 | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 0.800 J/cm2 | 3.81 ft-lb/in2 | ISO 179 | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179 | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 1.00e+6 Hz | 3.5 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | IEC 60250 | |||
| Dissipation Factor | 0.010 @Frequency 100 Hz | 0.010 @Frequency 100 Hz | IEC 60250 | ||
| 0.023 @Frequency 1.00e+6 Hz | 0.023 @Frequency 1.00e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 40.0 μm/m-°C @Temperature -30.0 - 30.0 °C | 22.2 μin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| CTE, linear, Parallel to Flow | 85.0 μm/m-°C | 47.2 μin/in-°F | ISO 11359 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 160 °C | 320 °F | ASTM Test | ||
| 160 °C | 320 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 54.0 °C | 129 °F | ASTM Test | ||
| 65.0 °C | 149 °F | ISO 75 | |||
| Vicat Softening Point | 204 °C | 399 °F | (50 °C/h / 50N) - B/50; ISO 306 | ||
| Glass Transition Temp, Tg | 60.0 °C | 140 °F | 10 K/min; ISO 11357-1/-3 | ||
| Oxygen Index | 26 % | 26 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| FDA | 21 CFR 177.1500 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Other Extrusion | ||||