- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 2.6
- 缺口沖擊強度: 5.0
- 彎曲強度 [MPa]: 115.0
- 彎曲模量 [MPa]: 5.30
- 熱變形溫度 [℃]: 217.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in3 | ISO 1183 | ||
| Water Absorption | 2.6 % | 2.6 % | 24 hour; ISO Test | ||
| 8.0 % | 8.0 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.6 % | 2.6 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 115 MPa | 16700 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 6.06 GPa | 879 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 5.30 GPa | 769 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 5.00 kJ/m2 | 2.38 ft-lb/in2 | ISO Test | ||
| 4.50 kJ/m2 @Temperature -40.0 °C | 2.14 ft-lb/in2 @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact, Notched | 0.500 J/cm2 | 2.38 ft-lb/in2 | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 217 °C | 423 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK00564 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||