- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 0.9
- 缺口沖擊強度: 1.05
- 彎曲強度 [MPa]: 140.0
- 彎曲模量 [MPa]: 7.50
- 硬度: 121.0
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in3 | ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.5 % | 5.5 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 23°C/50% R.H.; ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 150 MPa | 21800 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 140 MPa | 20300 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 9.10 GPa | 1320 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 210 MPa | 30500 psi | ISO Data | ||
| 240 MPa | 34800 psi | ASTM Test | |||
| Flexural Modulus | 7.50 GPa | 1090 ksi | ISO Data | ||
| 8.14 GPa | 1180 ksi | ASTM Test | |||
| Izod Impact, Notched | 1.05 J/cm @Temperature -40.0 °C | 1.97 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 2.10 J/cm @Thickness 3.17 mm | 3.93 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Notched (ISO) | 19.0 kJ/m2 | 9.04 ft-lb/in2 | ISO Test | ||
| 13.0 kJ/m2 @Temperature -40.0 °C | 6.19 ft-lb/in2 @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 7.10 J/cm2 | 33.8 ft-lb/in2 | ISO 179 | ||
| Charpy Impact, Notched | 1.80 J/cm2 | 8.57 ft-lb/in2 | ISO 179 | ||
| 1.00 J/cm2 @Temperature -30.0 °C | 4.76 ft-lb/in2 @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO 75 | ||
| 210 °C | 410 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| UL.UL-C | Yes | ||||