- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 0.9
- 彎曲強度 [MPa]: 90.0
- 彎曲模量 [MPa]: 5.03
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in3 | dry; ISO 1183 | ||
| Water Absorption | 0.90 % | 0.90 % | 24 hour; ISO Test | ||
| 5.5 % | 5.5 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 90.0 MPa | 13100 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 90.0 MPa | 13100 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 6.0 % | 6.0 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 4.61 GPa | 669 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 120 MPa | 17400 psi | ISO Data | ||
| Flexural Modulus | 5.03 GPa | 730 ksi | ISO Data | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||
| UL.UL-C | Yes | ||||