- 拉伸強度 [MPa]: 62.1
- 彎曲模量 [MPa]: 4.395
- 熱變形溫度 [℃]: 185.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.32 g/cc | 1.32 g/cc | ISO 1183/1 |
| Linear Mold Shrinkage | 0.011 cm/cm @Thickness 3.175 mm | 0.011 in/in @Thickness 0.1250 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 60.0 MPa | 8700 psi | ISO 527 |
| Tensile Strength, Yield | 62.1 MPa | 9000 psi | ISO 527 |
| Flexural Strength | 109 MPa | 15800 psi | ISO 178 |
| Flexural Modulus | 4.395 GPa | 637.4 ksi | ISO 178 |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 185 °C | 365 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 73.9 °C | 165 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 270 - 295 °C | 518 - 563 °F | |
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |
| Drying Temperature | 79.4 °C | 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | Predrying |