- 密度 [g/cm3]: 1.56
- 缺口沖擊強度: 0.48
- 彎曲強度 [MPa]: 94.0
- 彎曲模量 [MPa]: 7.40
- 硬度: 118.0
- 熱變形溫度 [℃]: 192.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in3 | |
| Linear Mold Shrinkage | 0.0040 cm/cm | 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 94.0 MPa | 13600 psi | ASTM D638 |
| Elongation at Break | 3.4 % | 3.4 % | ASTM D638 |
| Flexural Strength | 144 MPa | 20900 psi | ASTM D790 |
| Flexural Modulus | 7.40 GPa | 1070 ksi | ASTM D790 |
| Izod Impact, Notched | 0.480 J/cm | 0.899 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 2.46 J/cm | 4.61 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 205 - 225 °C | 401 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 192 °C | 378 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 175 °C | 347 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 271 °C | 500 - 520 °F | Approximate middle barrel temperature range |