- 密度 [g/cm3]: 1.33
- 缺口沖擊強(qiáng)度: 0.27
- 彎曲強(qiáng)度 [MPa]: 70.0
- 彎曲模量 [MPa]: 4.50
- 硬度: 110.0
- 熱變形溫度 [℃]: 193.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.33 g/cc | 0.0480 lb/in3 | |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Ultimate | 70.0 MPa | 10200 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 145 MPa | 21000 psi | ASTM D790 |
| Flexural Modulus | 4.50 GPa | 653 ksi | ASTM D790 |
| Izod Impact, Notched | 0.270 J/cm | 0.506 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | NB | NB | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 205 - 225 °C | 401 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 193 °C | 379 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 114 °C | 237 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 271 °C | 500 - 520 °F | Approximate middle barrel temperature range |