- 密度 [g/cm3]: 1.25
- 缺口沖擊強度: 0.69
- 彎曲強度 [MPa]: 60.0
- 彎曲模量 [MPa]: 3.00
- 硬度: 110.0
- 熱變形溫度 [℃]: 172.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.25 g/cc | 0.0452 lb/in3 | |
| Linear Mold Shrinkage | 0.011 cm/cm | 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 110 | 110 | ASTM D785 |
| Tensile Strength, Ultimate | 60.0 MPa | 8700 psi | ASTM D638 |
| Elongation at Break | 12 % | 12 % | ASTM D638 |
| Flexural Strength | 83.0 MPa | 12000 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Izod Impact, Notched | 0.690 J/cm | 1.29 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 5.23 J/cm | 9.80 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 205 - 225 °C | 401 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 172 °C | 342 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 106 °C | 223 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 271 °C | 500 - 520 °F | Approximate middle barrel temperature range |