- 密度 [g/cm3]: 1.57
- 缺口沖擊強度: 1.12
- 彎曲強度 [MPa]: 145.0
- 彎曲模量 [MPa]: 11.0
- 硬度: 118.0
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.57 g/cc | 0.0567 lb/in3 | |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 118 | 118 | ASTM D785 |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | ASTM D638 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638 |
| Flexural Strength | 234 MPa | 33900 psi | ASTM D790 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ASTM D790 |
| Izod Impact, Notched | 1.12 J/cm | 2.10 ft-lb/in | ASTM D256 |
| Izod Impact, Unnotched | 8.54 J/cm | 16.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 205 - 225 °C | 401 - 437 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 260 - 271 °C | 500 - 520 °F | Approximate middle barrel temperature range |