- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 拉伸強(qiáng)度 [MPa]: 36.0
- 彎曲模量 [MPa]: 0.770
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in3 | dry; ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hour; ISO Test | ||
| 9.5 % | 9.5 % | beginning dry; ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | beginning dry (23°C/50% R.H.); ISO 62 | ||
| Relative Viscosity | 2.6 cP | 2.6 cP | ISO Test; 96 % SAV | ||
| Viscosity Measurement | 48 | 48 | Formic Acid | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50mm/min; ISO 527 | ||
| 36.0 MPa | 5220 psi | 2 in/min; ASTM Test | |||
| Elongation at Break | >= 50 % | >= 50 % | 50mm/min, Nominal strain; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM Test | |||
| Elongation at Yield | 16 % | 16 % | 50mm/min; ISO 527 | ||
| 16 % | 16 % | 2 in/min; ASTM Test | |||
| Tensile Modulus | 0.970 GPa | 141 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 25.0 MPa | 3630 psi | ISO Data | ||
| 35.0 MPa | 5080 psi | ASTM Test | |||
| Flexural Modulus | 0.770 GPa | 112 ksi | ISO Data | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | BK-102 | ||||
| Commercial Status | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||
| UL.UL-C | Yes | ||||