- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 3.0
- 彎曲強度 [MPa]: 80.0
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | |
| Water Absorption | 3.0 % | 3.0 % | |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | Humidity Absorption |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | 5 mm/min |
| Elongation at Break | 4.8 % | 4.8 % | 5 mm/min |
| Tensile Modulus | 3.30 GPa | 479 ksi | 1 mm/min |
| Tensile Creep Modulus, 1 hour | 2530 MPa | 367000 psi | |
| Tensile Creep Modulus, 1000 hours | 1790 MPa | 260000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 2.6 @Frequency 100 Hz | 2.6 @Frequency 100 Hz | |
| 3.2 @Frequency 1e+6 Hz | 3.2 @Frequency 1e+6 Hz | ||
| Dielectric Strength | 36.0 kV/mm | 914 kV/in | |
| Dissipation Factor | 0.024 @Frequency 1e+6 Hz | 0.024 @Frequency 1e+6 Hz | |
| 0.063 @Frequency 100 Hz | 0.063 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||