- 熔體流動速率 [g/10min]: 6.0
- 密度 [g/cm3]: 1.12
- 吸水率 [%]: 0.8
- 拉伸強度 [MPa]: 84.0
- 彎曲強度 [MPa]: 80.0
- 彎曲模量 [MPa]: 3.00
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in3 | ISO R1183 |
| Water Absorption | 0.80 % | 0.80 % | 23°C / 24 hrs; ISO 62 |
| Moisture Absorption at Equilibrium | 1.2 % | 1.2 % | 23°C / 50% RH; ISO 62 |
| 2.9 % | 2.9 % | in 23°C water; ISO 62 | |
| Melt Flow | 6.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 6.0 g/10 min @Load 4.76 lb, Temperature 455 °F | after drying; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 81 | 81 | ISO 868 |
| Tensile Strength, Ultimate | 80.0 MPa | 11600 psi | ISO R527 |
| Tensile Strength, Yield | 84.0 MPa | 12200 psi | ISO R527 |
| Elongation at Break | 4.8 % | 4.8 % | ISO R527 |
| Elongation at Yield | 3.7 % | 3.7 % | ISO R527 |
| Modulus of Elasticity | 3.30 GPa | 479 ksi | ISO R527 |
| Flexural Strength | 110 MPa | 16000 psi | After conditioning at 23°C and 50% RH; ISO 178 |
| 185 MPa | 26800 psi | Dry; ISO 178 | |
| Flexural Modulus | 3.00 GPa | 435 ksi | After conditioning at 23°C and 50% RH; ISO 178 |
| 3.20 GPa | 464 ksi | Dry; ISO 178 | |
| Charpy Impact, Notched | 2.10 J/cm2 | 9.99 ft-lb/in2 | After conditioning at 23°C/50%RH; ISO 179/Af |
| 2.00 J/cm2 @Temperature 23.0 °C | 9.52 ft-lb/in2 @Temperature 73.4 °F | Dry; ISO 179/Af | |
| 19.5 J/cm2 @Temperature -20.0 °C | 92.8 ft-lb/in2 @Temperature -4.00 °F | Dry; ISO 179/Af | |
| 20.0 J/cm2 @Temperature -20.0 °C | 95.2 ft-lb/in2 @Temperature -4.00 °F | After conditioning at 23°C/50%RH; ISO 179/Af | |
| Tensile Creep Modulus, 1 hour | 2530 MPa | 367000 psi | ISO 899-1 |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.40e+15 ohm-cm | 1.40e+15 ohm-cm | ASTM D257 |
| Surface Resistance | 3.10e+15 ohm | 3.10e+15 ohm | ASTM D257 |
| Dielectric Strength | 36.0 kV/mm @Thickness 1.00 mm | 914 kV/in @Thickness 0.0394 in | ASTM D149 |
| Dissipation Factor | 0.024 @Frequency 100000 Hz | 0.024 @Frequency 100000 Hz | NFC 26 230 |
| 0.063 @Frequency 100 Hz | 0.063 @Frequency 100 Hz | NFC 26 230 | |
| 0.065 @Frequency 1000 Hz | 0.065 @Frequency 1000 Hz | NFC 26 230 | |
| Comparative Tracking Index | >= 600 V | >= 600 V | NFC 26 220 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ISO R1218 |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO R75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO R75 |
| Flammability, UL94 | HB | HB | |