- 透光率 [%]: 88.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 100 g/m2/day | 6.44 g/100 in2/day | 104°F (40°C) / 90%RH; ASTM E96 |
| Oxygen Transmission Rate | 1.50 cc/m2/day | 0.0966 cc/100 in2/day | 68°F (20°C) / 65%RH; ASTM D3985 |
| Thickness | 15.2 microns | 0.600 mil | |
| Surface Tension | 36 - 38 dynes/cm | 36 - 38 dynes/cm | untreated side; ASTM D2578 |
| >= 46 dynes/cm | >= 46 dynes/cm | treated side; ASTM D2578 | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 110 % | 110 % | ASTM D882 |
| Film Elongation at Break, TD | 100 % | 100 % | ASTM D882 |
| Secant Modulus, MD | 1.60 GPa | 232 ksi | ASTM D882 |
| Secant Modulus, TD | 1.50 GPa | 218 ksi | ASTM D882 |
| Coefficient of Friction | 0.15 | 0.15 | film to stainless steel; ASTM D1894 |
| 0.50 | 0.50 | film to film; ASTM D1894 | |
| Film Tensile Strength at Break, MD | 190 MPa | 27600 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 200 MPa | 29000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Shrinkage, MD | 1.6 % | 1.6 % | hot air, 320°F/160°C - 5 min. |
| 2.8 % | 2.8 % | hot water, 203°F/95°C - 5 min. | |
| Shrinkage, TD | 0.30 % | 0.30 % | hot air, 320°F/160°C - 5 min. |
| 1.4 % | 1.4 % | hot water, 203°F/95°C - 5 min. | |
| Optical Properties | Metric | English | Comments |
| Haze | 4.0 % | 4.0 % | ASTM D1003 |
| Gloss | 170 % | 170 % | at 20°; ASTM D523 |
| Transmission, Visible | 88 % | 88 % | |