- 密度 [g/cm3]: 1.44
- 吸水率 [%]: 1.0
- 彎曲強(qiáng)度 [MPa]: 170.0
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in3 | ISO data |
| Water Absorption | 1.0 % | 1.0 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.7 % | 5.7 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage, Flow | 0.0020 cm/cm | 0.0020 in/in | ASTM and ISO value |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 3.0 % | 3.0 % | Strain at break, ISO, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 12.5 GPa | 1810 ksi | same value from ASTM and ISO test. |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 4.60 GPa | 667 ksi | calculated |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 20.0 μm/m-°C @Temperature 20.0 °C | 11.1 μin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 60.0 μm/m-°C @Temperature 20.0 °C | 33.3 μin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO Data |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |