- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 1.4
- 斷裂伸長率 [%]: 235
- 彎曲強度 [MPa]: 150.0
- 彎曲模量 [MPa]: 8.14
- 熱變形溫度 [℃]: 194.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ISO data |
| Water Absorption | 1.4 % | 1.4 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 8.2 % | 8.2 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM data at 5 mm/min. |
| 152 MPa | 22000 psi | ISO value at 5mm/min. | |
| Elongation at Break | 4.0 % | 4.0 % | Strain at break, ISO, 5 mm/min |
| 4.0 % | 4.0 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 235 MPa | 34100 psi | ASTM Data |
| Flexural Modulus | 8.14 GPa | 1180 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ASTM Data |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |