- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 1.1
- 斷裂伸長率 [%]: 245
- 彎曲強(qiáng)度 [MPa]: 160.0
- 彎曲模量 [MPa]: 8.30
- 熱變形溫度 [℃]: 194.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in3 | ISO data |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 6.7 % | 6.7 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 160 MPa | 23200 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 4.5 % | 4.5 % | Strain at break, ISO, 5 mm/min |
| 4.5 % | 4.5 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 245 MPa | 35500 psi | ASTM Data |
| Flexural Modulus | 8.30 GPa | 1200 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 194 °C | 381 °F | ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ASTM Data |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |