- 斷裂伸長(zhǎng)率 [%]: 190
- 彎曲強(qiáng)度 [MPa]: 120.0
- 彎曲模量 [MPa]: 5.10
- 熱變形溫度 [℃]: 186.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | ASTM data at 5 mm/min. |
| Flexural Yield Strength | 190 MPa | 27600 psi | ASTM Data |
| Flexural Modulus | 5.10 GPa | 740 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM test |
| Deflection Temperature at 0.46 MPa (66 psi) | 186 °C | 367 °F | ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 214 °C | 417 °F | ASTM Data |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |