- 密度 [g/cm3]: 1.34
- 拉伸強度 [MPa]: 6.0
- 斷裂伸長率 [%]: 150
- 彎曲強度 [MPa]: 100.0
- 彎曲模量 [MPa]: 5.24
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in3 | (Dry) |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 100 MPa | 14500 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 6.00 MPa | 870 psi | ISO value; stress at 50% strain at 50 mm/min. |
| 98.0 MPa | 14200 psi | ISO value at 50 mm/min. | |
| 100 MPa | 14500 psi | ASTM test value at 50 mm/min. | |
| Elongation at Break | 6.0 % | 6.0 % | Strain at break, ASTM, 5 mm/min |
| Elongation at Yield | 5.3 % | 5.3 % | ISO Value at 50 mm/min. |
| 5.5 % | 5.5 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 6.30 GPa | 914 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 150 MPa | 21800 psi | ASTM Data |
| Flexural Modulus | 5.24 GPa | 760 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |