- 密度 [g/cm3]: 1.34
- 吸水率 [%]: 0.9
- 斷裂伸長率 [%]: 235
- 彎曲強度 [MPa]: 150.0
- 彎曲模量 [MPa]: 8.00
- 熱變形溫度 [℃]: 219.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.34 g/cc | 0.0484 lb/in3 | ISO data |
| Water Absorption | 0.90 % | 0.90 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.5 % | 1.5 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.4 % | 5.4 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ISO data |
| 0.0030 cm/cm | 0.0030 in/in | ASTM data MD | |
| Linear Mold Shrinkage, Transverse | 0.0090 cm/cm | 0.0090 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 150 MPa | 21800 psi | ASTM data at 5 mm/min. |
| 152 MPa | 22000 psi | ISO value at 5mm/min. | |
| Elongation at Break | 3.5 % | 3.5 % | Strain at break, ASTM, 5 mm/min |
| 3.5 % | 3.5 % | Strain at break, ISO, 5 mm/min | |
| Tensile Modulus | 9.41 GPa | 1360 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 235 MPa | 34100 psi | ASTM Data |
| Flexural Modulus | 8.00 GPa | 1160 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 3.50 GPa | 508 ksi | calculated |
| Charpy Impact, Notched | 1.90 J/cm2 | 9.04 ft-lb/in2 | ISO Data |
| 1.40 J/cm2 @Temperature -30.0 °C | 6.66 ft-lb/in2 @Temperature -22.0 °F | ISO data | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 24.0 μm/m-°C @Temperature 20.0 °C | 13.3 μin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 84.0 μm/m-°C @Temperature 20.0 °C | 46.7 μin/in-°F @Temperature 68.0 °F | ISO data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 219 °C | 426 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO data |
| 210 °C | 410 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 0.800 mm | HB @Thickness 0.0315 in | |
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |