- 密度 [g/cm3]: 1.174
- 吸水率 [%]: 1.1
- 斷裂伸長率 [%]: 290
- 彎曲強度 [MPa]: 189.0
- 彎曲模量 [MPa]: 8.41
- 熱變形溫度 [℃]: 220.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.174 g/cc | 0.04241 lb/in3 | Melt Density |
| 1.36 g/cc | 0.0491 lb/in3 | ISO data | |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 6.6 % | 6.6 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ISO data |
| 0.0030 cm/cm | 0.0030 in/in | ASTM data MD | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO Data |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 189 MPa | 27400 psi | ISO value at 5mm/min. |
| 190 MPa | 27600 psi | ASTM data at 5 mm/min. | |
| Elongation at Break | 3.5 % | 3.5 % | Strain at break, ISO, 5 mm/min |
| 3.5 % | 3.5 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 9.65 GPa | 1400 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 290 MPa | 42100 psi | ASTM Data |
| Flexural Modulus | 8.41 GPa | 1220 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 3.60 GPa | 522 ksi | calculated |
| Charpy Impact, Notched | 1.35 J/cm2 | 6.42 ft-lb/in2 | ISO Data |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | >= 1.00e+15 ohm-cm | >= 1.00e+15 ohm-cm | ISO data |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 25.0 μm/m-°C @Temperature 20.0 °C | 13.9 μin/in-°F @Temperature 68.0 °F | ISO data |
| CTE, linear, Transverse to Flow | 70.0 μm/m-°C @Temperature 20.0 °C | 38.9 μin/in-°F @Temperature 68.0 °F | ISO data |
| Specific Heat Capacity | 1.89 J/g-°C | 0.452 BTU/lb-°F | Melt value |
| Thermal Conductivity | 0.230 W/m-K | 1.60 BTU-in/hr-ft2-°F | Melt |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 205 °C | 401 °F | ISO data |
| 209 °C | 408 °F | ASTM Data | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |