- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 1.1
- 斷裂伸長率 [%]: 175
- 彎曲強度 [MPa]: 110.0
- 彎曲模量 [MPa]: 4.83
- 熱變形溫度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ISO data |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 7.1 % | 7.1 % | in water; 23°C; ISO data |
| Viscosity Measurement | 31 | 31 | Formic Acid Viscosity; ISO data |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 3.2 % | 3.2 % | Strain at break, ISO, 5 mm/min |
| 3.5 % | 3.5 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 5.61 GPa | 814 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 175 MPa | 25400 psi | ASTM Data |
| Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Shear Modulus | 2.10 GPa | 305 ksi | calculated |
| Charpy Impact, Notched | 1.30 J/cm2 | 6.19 ft-lb/in2 | ISO Data |
| 0.610 J/cm2 @Temperature -30.0 °C | 2.90 ft-lb/in2 @Temperature -22.0 °F | ISO data | |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO data |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO Data |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |