- 密度 [g/cm3]: 1.36
- 拉伸強度 [MPa]: 107.0
- 彎曲強度 [MPa]: 115.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in3 | (Dry) |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | ASTM data at 5 mm/min. |
| Tensile Strength, Yield | 107 MPa | 15500 psi | ISO value at 50 mm/min. |
| 110 MPa | 16000 psi | ASTM value at 50 mm/min. | |
| Elongation at Break | 6.0 % | 6.0 % | Nominal strain at break, ISO, 50 mm/min |
| 6.0 % | 6.0 % | Strain at break, ASTM, 5 mm/min | |
| Elongation at Yield | 5.9 % | 5.9 % | ISO Value at 50 mm/min. |
| 6.0 % | 6.0 % | ASTM Value at 50 mm/min. | |
| Tensile Modulus | 4.92 GPa | 714 ksi | same value from ASTM and ISO test. |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |