- 密度 [g/cm3]: 1.109
- 吸水率 [%]: 5.8
- 拉伸強度 [MPa]: 75.0
- 斷裂伸長率 [%]: 120
- 彎曲模量 [MPa]: 4.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.109 g/cc | 0.04007 lb/in3 | Melt Density |
| 1.43 g/cc | 0.0517 lb/in3 | ISO data | |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 5.8 % | 5.8 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ASTM value at 50 mm/min. |
| 76.0 MPa | 11000 psi | ISO value at 50 mm/min. | |
| Elongation at Break | 17 % | 17 % | Nominal strain at break, ISO, 50 mm/min |
| 20 % | 20 % | Nominal strain at break, ASTM, 50 mm/min | |
| Flexural Yield Strength | 120 MPa | 17400 psi | ASTM Data |
| Flexural Modulus | 4.00 GPa | 580 ksi | ISO Value |
| 4.485 GPa | 650.5 ksi | ASTM Value | |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Specific Heat Capacity | 2.77 J/g-°C | 0.662 BTU/lb-°F | Melt value |
| Thermal Conductivity | 0.234 W/m-K | 1.62 BTU-in/hr-ft2-°F | Melt |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 84.0 °C | 183 °F | ASTM Data |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |