- 密度 [g/cm3]: 1.43
- 吸水率 [%]: 1.0
- 拉伸強度 [MPa]: 90.0
- 斷裂伸長率 [%]: 130
- 彎曲模量 [MPa]: 5.00
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.43 g/cc | 0.0517 lb/in3 | ISO data |
| Water Absorption | 1.0 % | 1.0 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 1.8 % | 1.8 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 6.3 % | 6.3 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | 50 mm/min; Same value from ASTM and ISO test. |
| Elongation at Break | 15 % | 15 % | Nominal strain at break, ASTM, 50 mm/min |
| Flexural Yield Strength | 130 MPa | 18900 psi | ASTM Data |
| Flexural Modulus | 5.00 GPa | 725 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Coefficient of Friction | 0.15 | 0.15 | vs. steel. |
| 0.22 | 0.22 | vs. polymer | |
| Coefficient of Friction, Static | 0.23 | 0.23 | vs. steel. |
| 0.41 | 0.41 | vs. polymer | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 54.0 μm/m-°C @Temperature 20.0 °C | 30.0 μin/in-°F @Temperature 68.0 °F | ASTM data |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Deflection Temperature at 1.8 MPa (264 psi) | 117 °C | 243 °F | ASTM Data |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |