- 密度 [g/cm3]: 1.2
- 吸水率 [%]: 1.1
- 斷裂伸長率 [%]: 170
- 彎曲強(qiáng)度 [MPa]: 105.0
- 彎曲模量 [MPa]: 4.83
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.20 g/cc | 0.0434 lb/in3 | ISO data |
| Water Absorption | 1.1 % | 1.1 % | 24 hrs; ISO data |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | 50% RH; 23°C; ISO data |
| Water Absorption at Saturation | 7.1 % | 7.1 % | in water; 23°C; ISO data |
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data MD |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 105 MPa | 15200 psi | Same value from ASTM and ISO tests; 5 mm/min. |
| Elongation at Break | 2.8 % | 2.8 % | Strain at break, ISO, 5 mm/min |
| 3.0 % | 3.0 % | Strain at break, ASTM, 5 mm/min | |
| Flexural Yield Strength | 170 MPa | 24700 psi | ASTM Data |
| Flexural Modulus | 4.83 GPa | 701 ksi | ASTM Data |
| Poissons Ratio | 0.35 | 0.35 | ISO data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | ASTM and ISO test |
| Processing Properties | Metric | English | Comments |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |