- 密度 [g/cm3]: 1.39
- 斷裂伸長率 [%]: 190
- 彎曲強度 [MPa]: 115.0
- 彎曲模量 [MPa]: 6.12
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.39 g/cc | 0.0502 lb/in3 | (Dry) |
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data MD (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 115 MPa | 16700 psi | ISO value at 5mm/min. |
| 120 MPa | 17400 psi | ASTM data at 5 mm/min. | |
| Elongation at Break | 5.0 % | 5.0 % | Strain at break, ISO, 5 mm/min |
| 5.0 % | 5.0 % | Strain at break, ASTM, 5 mm/min | |
| Tensile Modulus | 6.94 GPa | 1010 ksi | same value from ASTM and ISO test. |
| Flexural Yield Strength | 190 MPa | 27600 psi | ASTM Data |
| Flexural Modulus | 6.12 GPa | 888 ksi | ASTM Data |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |