- 吸水率 [%]: 1.3
- 缺口沖擊強度: 0.534
- 彎曲模量 [MPa]: 1.31
- 熱變形溫度 [℃]: 221.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.14 g/cc | 1.14 g/cc | ASTM D792 |
| Water Absorption | 1.3 % @Time 86400 sec | 1.3 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.014 - 0.019 cm/cm @Thickness 3.17 mm | 0.014 - 0.019 in/in @Thickness 0.125 in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 60 | 60 | Conditioned; ASTM D785 |
| 85 | 85 | ASTM D785 | |
| Tensile Strength at Break | 65.5 MPa | 9500 psi | Conditioned; D638 |
| 82.7 MPa | 12000 psi | D638 | |
| Elongation at Break | 30 % | 30 % | ASTM D638 |
| 200 % | 200 % | Conditioned; ASTM D638 | |
| Flexural Strength | 40.7 MPa | 5900 psi | Conditioned; ASTM D790 |
| 114 MPa | 16500 psi | ASTM D790 | |
| Flexural Modulus | 1.31 GPa | 190 ksi | Conditioned; ASTM D790 |
| 3.03 GPa | 440 ksi | ASTM D790 | |
| Izod Impact, Notched | 0.534 J/cm | 1.00 ft-lb/in | ASTM D256 |
| 1.33 J/cm | 2.50 ft-lb/in | Conditioned; ASTM D256 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | Conditioned; ASTM D257 |
| 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | ASTM D257 | |
| Dielectric Constant | 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | ASTM D150 |
| 6.0 @Frequency 100 Hz | 6.0 @Frequency 100 Hz | Conditioned; ASTM D150 | |
| Dielectric Strength | 21.7 kV/mm | 550 kV/in | Conditioned; ASTM D149 |
| 22.8 kV/mm | 580 kV/in | Method A (Short-time); ASTM D149 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 82.8 μm/m-°C | 46.0 μin/in-°F | ASTM D696 |
| Deflection Temperature at 0.46 MPa (66 psi) | 221 °C | 430 °F | Unannealed, Conditioned; ASTM D648 |
| 238 °C | 460 °F | Unannealed; ASTM D648 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 71.1 °C | 160 °F | Unannealed, Conditioned; ASTM D648 |
| 87.8 °C | 190 °F | Unannealed; ASTM D648 | |
| Flammability, UL94 | V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | Conditioned |
| V-2 @Thickness 1.50 mm | V-2 @Thickness 0.0591 in | ||
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 271 - 293 °C | 520 - 560 °F | |
| Mold Temperature | 48.9 - 93.3 °C | 120 - 200 °F | |
| Drying Temperature | 73.9 °C @Time 7200 - 14400 sec | 165 °F @Time 2.00 - 4.00 hour | |
| Moisture Content | <= 0.20 % | <= 0.20 % | Suggested Maximum |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi | |
| Screw Speed | 40 - 140 rpm | 40 - 140 rpm | |