- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 2.6
- 缺口沖擊強度: 6.0
- 拉伸強度 [MPa]: 55.0
- 彎曲模量 [MPa]: 2.80
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 2.6 % @Temperature 23.0 °C | 2.6 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage, Flow | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.013 cm/cm @Thickness 2.00 mm | 0.013 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 84.0 MPa @Temperature 23.0 °C | 12200 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 35 % @Temperature 23.0 °C | 35 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| >= 50 % @Temperature 23.0 °C | >= 50 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |||
| >= 100 % @Temperature 23.0 °C | >= 100 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| Elongation at Yield | 4.3 % @Temperature 23.0 °C | 4.3 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 29 % @Temperature 23.0 °C | 29 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.20 GPa @Temperature 23.0 °C | 174 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| Izod Impact, Notched (ISO) | 6.00 kJ/m2 @Temperature 23.0 °C | 2.86 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 180/1A | ||
| Charpy Impact Unnotched | NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.400 J/cm2 @Temperature -30.0 °C | 1.90 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 0.600 J/cm2 @Temperature -30.0 °C | 2.86 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.700 J/cm2 @Temperature 23.0 °C | 3.33 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 2.10 J/cm2 @Temperature 23.0 °C | 9.99 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm @Temperature 23.0 °C | 1.00e+13 ohm-cm @Temperature 73.4 °F | 50%RH; IEC 60093 | ||
| >= 1.00e+15 ohm-cm @Temperature 23.0 °C | >= 1.00e+15 ohm-cm @Temperature 73.4 °F | DAM; IEC 60093 | |||
| Comparative Tracking Index | 600 V @Temperature 23.0 °C | 600 V @Temperature 73.4 °F | DAM; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| Oxygen Index | 20 % | 20 % | DAM; ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 285 °C | 545 °F | DAM; Optimum; Extrusion | |||
| 280 - 290 °C | 536 - 554 °F | DAM; Extrusion | |||
| 280 - 300 °C | 536 - 572 °F | DAM; Injection Molding | |||
| 290 °C | 554 °F | DAM; Optimum; Injection Molding | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum; Injection Molding | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Extrusion | ||
| 80.0 °C | 176 °F | DAM; Injection Molding | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Injection Molding | ||
| 4.00 - 6.00 hour | 4.00 - 6.00 hour | DAM; Extrusion | |||
| Moisture Content | <= 0.050 % | <= 0.050 % | DAM; Extrusion | ||
| <= 0.050 % | <= 0.050 % | DAM; Injection Molding | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66< | ISO 11469; DAM | |||
| Processing Method | Extrusion | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||