- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 2.6
- 拉伸強度 [MPa]: 55.0
- 彎曲模量 [MPa]: 1.20
- 硬度: 108.0
- 熱變形溫度 [℃]: 200.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in3 | DAM; ISO 1183 | ||
| Water Absorption | 2.6 % @Temperature 23.0 °C | 2.6 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 8.5 % @Temperature 23.0 °C | 8.5 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 3.20 mm | 0.015 in/in @Thickness 0.126 in | Flow; DAM | ||
| Linear Mold Shrinkage, Flow | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.014 cm/cm @Thickness 2.00 mm | 0.014 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 59 | 59 | 50%RH; ISO 2039/2 | ||
| 79 | 79 | DAM; ISO 2039/2 | |||
| Hardness, Rockwell R | 108 | 108 | 50%RH; ISO 2039/2 | ||
| 121 | 121 | DAM; ISO 2039/2 | |||
| Tensile Strength, Yield | 55.0 MPa @Temperature 23.0 °C | 7980 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 82.0 MPa @Temperature 23.0 °C | 11900 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Elongation at Break | 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | DAM; nominal; ISO 527 | ||
| 45 % @Temperature 23.0 °C | 45 % @Temperature 73.4 °F | 50mm/min; DAM; ISO 527 | |||
| >= 100 % @Temperature 23.0 °C | >= 100 % @Temperature 73.4 °F | 50%RH; nominal; ISO 527 | |||
| Elongation at Yield | 4.5 % @Temperature 23.0 °C | 4.5 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| 25 % @Temperature 23.0 °C | 25 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 1.40 GPa @Temperature 23.0 °C | 203 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 3.10 GPa @Temperature 23.0 °C | 450 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 1.20 GPa @Temperature 23.0 °C | 174 ksi @Temperature 73.4 °F | 50%RH; ISO 178 | ||
| 2.80 GPa @Temperature 23.0 °C | 406 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| Charpy Impact Unnotched | 40.0 J/cm2 @Temperature -30.0 °C | 190 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.300 J/cm2 @Temperature -30.0 °C | 1.43 ft-lb/in2 @Temperature -22.0 °F | 50%RH; ISO 179/1eA | ||
| 0.450 J/cm2 @Temperature -30.0 °C | 2.14 ft-lb/in2 @Temperature -22.0 °F | DAM; ISO 179/1eA | |||
| 0.550 J/cm2 @Temperature 23.0 °C | 2.62 ft-lb/in2 @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 1.50 J/cm2 @Temperature 23.0 °C | 7.14 ft-lb/in2 @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Tensile Creep Modulus, 1 hour | 1400 MPa @Temperature 23.0 °C | 203000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Tensile Creep Modulus, 1000 hours | 820 MPa @Temperature 23.0 °C | 119000 psi @Temperature 73.4 °F | 50%RH; ISO 899 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 μm/m-°C @Temperature 23.0 - 55.0 °C | 278 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 110 μm/m-°C @Temperature 23.0 - 55.0 °C | 61.1 μin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 200 °C | 392 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | DAM; ISO 75-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 290 °C | 554 °F | DAM; Optimum | |||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| Mold Temperature | 70.0 °C | 158 °F | DAM; optimum | ||
| 50.0 - 90.0 °C | 122 - 194 °F | DAM | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Appearance | Natural Color | DAM | |||
| Features | Food Contact Acceptable | DAM | |||
| Lubricated | DAM | ||||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66< | ISO 11469; DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Food Contact Resins | DAM | |||
| Unreinforced Resins | DAM | ||||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA66 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Uses | Food Applications, Non-specific | DAM | |||