- 吸水率 [%]: 0.98
- 成型收縮率 [%]: 0.015
- 缺口沖擊強度: 10.62
- 彎曲模量 [MPa]: 0.331
- 硬度: 70.0
- 熱變形溫度 [℃]: 98.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | DAM; ASTM D792 | ||
| Water Absorption | 0.98 % @Temperature 23.0 °C | 0.98 % @Temperature 73.4 °F | Immersion 24h; DAM; ASTM D570 | ||
| Linear Mold Shrinkage | 0.015 cm/cm @Thickness 3.20 mm | 0.015 in/in @Thickness 0.126 in | Transverse; DAM | ||
| 0.023 cm/cm @Thickness 3.20 mm | 0.023 in/in @Thickness 0.126 in | Flow; DAM | |||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 70 | 70 | 50%RH; ASTM D785 | ||
| 106 | 106 | DAM; ASTM D785 | |||
| Tensile Strength | 43.4 MPa @Temperature 23.0 °C | 6290 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 52.4 MPa @Temperature 23.0 °C | 7600 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Elongation at Break | 90 % @Temperature 23.0 °C | 90 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 200 % @Temperature 23.0 °C | 200 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| Flexural Modulus | 0.331 GPa @Temperature 100 °C | 48.0 ksi @Temperature 212 °F | DAM; ASTM D790 | ||
| 0.897 GPa @Temperature 23.0 °C | 130 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | |||
| 1.862 GPa @Temperature 23.0 °C | 270.1 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Notched | 10.62 J/cm @Temperature 23.0 °C | 19.90 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Unnotched | 10.6 J/cm @Temperature 23.0 °C | 19.9 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 260 °C | 500 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 98.0 °C | 208 °F | DAM; ASTM D648 | ||
| 98.0 °C | 208 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | DAM; ASTM D648 | ||
| 55.0 °C | 131 °F | DAM; ISO 75-1/-2 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 260 °C | 500 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 280 - 300 °C | 536 - 572 °F | DAM | |||
| 290 °C | 554 °F | DAM; Optimum | |||
| Mold Temperature | 50.0 - 90.0 °C | 122 - 194 °F | DAM | ||
| 70.0 °C | 158 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Forms | Pellets | DAM | |||
| Material Status | Preliminary Data | DAM | |||
| Processing Method | Extrusion | DAM | |||
| Product Category | Extrusion Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Unreinforced Resins | DAM | ||||
| RoHS Compliance | Contact Manufacturer | DAM | |||